Semiconductor device having low contact resistance

ABSTRACT

A semiconductor device capable of stably operating even at a low voltage, includes: a semiconductor substrate having a surface region of a first conductivity type; a conductive film directly formed on a surface of the surface region at an area thereof, the conductive film containing impurities of a second conductivity type opposite to the first conductivity type; an oozed diffusion region of the second conductivity type formed by diffusion of the impurities in the conductive film into the substrate, the oozed diffusion region being formed at an area contiguous to the conductive film in the surface region; a low resistivity region of the second conductivity type extending from an area adjacent to the conductive film in the surface region and overlapping the conductive film; and a DDD structure transistor formed on another region of the surface region, wherein a length of a portion of the low resistivity region overlapping the conductive film is substantially the same as a length of a portion of the deep source and drain regions of the DDD structure overlapping the gate electrode.

BACKGROUND OF THE INVENTION

a) Field of the Invention

The present invention relates to a method of manufacturing a semiconductor device, and more particularly to a technique allowing a semiconductor integrated circuit to reliably operate at a low voltage.

b) Description of the Related Art

In connecting a region in a semiconductor substrate to a wiring formed on the substrate, a highly doped region is generally formed in the surface of the substrate, and thereafter a wiring is connected to the surface of the highly doped region. As the material of wiring, metal, silicide, doped silicon, and other materials are used.

If a wiring is made of polycrystalline silicon or amorphous silicon, a simplified connection structure may be adopted. Specifically, a silicon electrode is first formed on the surface of a semiconductor substrate, and thereafter ions are implanted in the silicon electrode and semiconductor substrate adjacent thereto. The doped silicon electrode and doped region of the substrate contact slightly at the interface therebetween. Heat treatment at the later process diffuses impurities in the doped silicon electrode and substrate region toward the non-doped region under the silicon electrode, and electrical interconnect therebetween is established.

The above processes are advantageous in that they can be performed at the same time when a gate of a MOS transistor is formed and then ions are implanted to the source and drain regions.

Recent semiconductor integrated circuits with very fine patterns have a demand for a low voltage operation of the circuits. As the operating voltage lowers, a voltage difference between high and low levels (logic swing) becomes small and the circuit operation becomes likely to become unstable.

A circuit may become unstable at a low voltage such as 3 V or 3.3 V even if it operates stably at an operating voltage of 5 V.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide a semiconductor device manufacturing technique capable of providing a stable operation of a semiconductor integrated circuit even at a low voltage.

According to one aspect of the present invention, there is provided a semiconductor device including: a semiconductor substrate having a surface region of a first conductivity type; a conductive film directly formed on part of a surface of the surface region, the conductive film containing impurities of a second conductivity type opposite to the first conductivity type; an oozed diffusion or out-diffusion region of the second conductivity type formed by outward diffusion of the impurities in the conductive film, the oozed diffusion region being formed at an area contiguous to the conductive film in the surface region; a low resistivity region of the second conductivity type extending from an area adjacent to the conductive film in the surface region and overlapping the conductive film; and a double-diffused drain (DDD) structure transistor comprising a first gate electrode formed on a gate insulating film over a channel region defined by an area in the surface region, first source and drain regions of the second conductivity type formed on both sides of the first gate electrode, and second source and drain regions of the second conductivity type surrounding, and being formed deeper than, the first source and drain regions and overlapping the first gate electrode, wherein a length of a portion of the low resistivity region overlapping the conductive film is substantially the same as a length of a portion of the second source and drain regions overlapping the first gate electrode.

According to another aspect of the present invention, there is provided an SRAM semiconductor device including a parallel circuit of two serial circuits each having a driver transistor and a load, a wiring for connecting an interconnection point between the driver transistor and the load of each serial circuit to a gate electrode of the driver transistor of the other serial circuit, and a transfer transistor connected to each interconnection point, wherein the two driver transistors and two transfer transistors are each formed by a MISFET having a channel region formed in an active region of a first conductivity type in a surface of a semiconductor substrate, source and drain regions formed on both sides of the channel region, and an insulated gate electrode formed over the channel region, the SRAM semiconductor device including: a pair of wirings containing impurities of a second conductivity type opposite to the first conductivity type, each of the wirings being directly formed on part of a surface of the active region where the two driver transistors are formed; and a double-diffused drain (DDD) structure MISFET having a channel region defined in an active region of the first conductivity type in the surface of the semiconductor substrate, source and drain regions of a DDD structure formed on both sides of the channel region and having shallow source and drain regions and deep source and drain regions enveloping said shallow source and drain regions, and an insulated gate electrode formed over the channel region, and wherein regions where one of the source and drain regions of the two driver transistors, which is connected to the wiring, is formed to overlap the wiring from an end thereof, and a length of a portion of the source and drain regions overlapping the wiring is substantially the same as a length of a portion of the deep source and drain regions of the DDD structure overlapping the insulated gate electrode from an end thereof.

A low resistivity region doped with impurities and connected to a wiring directly formed on the surface of a semiconductor substrate adjacent to the low resistivity region, is formed by the same process of forming deep source and drain regions of a DDD structure. Impurities having a relatively large diffusion coefficient may be doped in the deep source and drain regions of the DDD structure. Therefore, impurities in the low resistivity region diffuse deeply and at the same time creep under and overlap the wiring. As a result, the connection area of the wiring and low resistivity region becomes large and the contact resistance can be lowered.

If the connection structure of the wiring and low resistance region is applied to the connection structure of a wiring and source and drain regions of a driver transistor of an SRAM semiconductor device, one of the source and drain regions of the driver transistor can be connected to a constant potential with a low contact resistance. It is therefore possible to provide an SRAM capable of reliably operating even at a low supply voltage.

If a DDD type MISFET is formed on the same chip, the semiconductor device capable of reliably operating at a low voltage can be formed by changing mask patterns without increasing the number of manufacturing processes.

As described above, a low resistivity region doped with impurities and a wiring directly formed on the surface of the semiconductor substrate adjacent to the low resistivity region can be electrically connected with a low contact resistance. Accordingly, it becomes possible to provide a semiconductor device capable of reliably operating even at a low voltage.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A to 1D are cross sectional views of substrates illustrating the structures of connection between a wiring and a low resistivity region.

FIG. 2 is a layout of a monitor circuit manufactured for evaluating embodiments of the invention.

FIGS. 3A and 3B are a circuit diagram of an SRAM cell to which the connection structure of an embodiment of the invention is applied, and a plan view of the SRAM cell on a semiconductor substrate.

FIGS. 4A to 4E are cross sectional views of a substrate taken along one-dot chain line IV--IV of FIG. 3B, explaining the processes of a method of manufacturing an SRAM cell by applying the connection structure of an embodiment of the invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The inventor has estimated the reason for an unstable operation of an integrated circuit at a low voltage to be ascribed to a large contact resistance between a wiring and a low resistivity region. The wiring is made of polycrystalline silicon or other materials and formed by the same process as that of forming a gate electrode of a MISFET, and the low resistivity region is formed thereafter by ion implantation.

Referring to FIGS. 1A to 1D, conventional connection structures between a wiring and a low resistivity region will first be described, and then connection structures between a wiring and a low resistivity region according to embodiments of the invention will be described.

FIG. 1A is a cross sectional view of a substrate showing the conventional connection structure between a wiring and a low resistivity region. A wiring 2 of polycrystalline silicon is formed on the surface of a semiconductor substrate 1. The wiring 2 is formed by the same process as that of forming a gate electrode of a MISFET on another region of the substrate 1. An outwardly diffused or oozed diffusion region 4 is formed just under the wiring 2 by outward diffusion of impurities from the wiring 2 to the substrate 1 by heat treatment performed after the wiring 2 was formed.

Low resistivity regions 3 are formed on both the sides of the wiring 2 by ion implantation. The low resistivity region 3 may be formed at the same time when the source and drain regions of MISFET are formed together with the doping of a polycrystalline silicon gate. Since ion implantation is performed after the wiring 2 was formed, no low resistivity region is formed just under the wiring 2. However, in addition to a small lateral diffusion at the time of ion implantation, later heat treatment causes impurities to diffuse in the lateral direction. This lateral diffusion region overlaps the oozed diffusion region 4.

The wiring 2 and the low resistivity regions 3 are electrically connected together by an overlap region 5 of the low resistivity region 3 and oozed diffusion region 4. If thermal hysteresis is different, diffusion of the oozed diffusion region 4 and low resistivity region 3 becomes different. If the area of the overlap region 5 becomes small because of variation of diffusion, the contact resistance becomes high.

The source and drain regions of a transistor, particularly in recent semiconductor devices with very fine patterns, are made shallow in order to alleviate the short channel effect. There is therefore a tendency that the resistance of the overlap region 5 is becoming smaller and smaller.

FIG. 1B shows the conventional connection structure between a wiring and a low resistivity region wherein a MISFET of a lightly doped drain (LDD) structure is formed in another region of the semiconductor substrate.

A wiring and low resistivity regions on both the sides of the wiring are formed by the same processes as those of forming a gate electrode and source and drain regions of MISFET of the LDD structure. Side wall regions 6 are therefore formed on the side walls of the wiring layer 2. A low concentration region 3a having an impurity concentration lower than the low resistivity region 3 is therefore formed just under the side wall 6.

The contact resistance becomes high because the low concentration region 3a is serially inserted between the wiring 2 and low resistivity region 3. As described above, if an LDD structure is formed in the same substrate, the contact resistance becomes higher than the case explained with FIG. 1A. As semiconductor devices are made finer and finer, an LDD structure is often used so as not to deteriorate the device performance by hot electrons. An increase of the contact resistance between the wiring 2 and low resistivity region 3 may become a significant issue.

Next, with reference to FIGS. 1C and 1D, the fundamental structure according to embodiments of the invention will be described.

FIG. 1C shows a fundamental structure wherein a usual MISFET is formed in the same substrate. A deeper low resistivity region 7 is formed under a low resistivity region 3, the former region 7 enveloping or surrounding the latter region 3. Other structures are similar to those in FIG. 1A.

FIG. 1D shows another fundamental structure wherein a MISFET of an LDD structure is formed in the same substrate. Similar to FIG. 1C, a deeper low resistivity region 7 is formed under a low resistivity region 3, the former region 7 enclosing or surrounding the latter region 3. Other structures are similar to those in FIG. 1B.

The deeper low resistivity regions 7 shown in FIGS. 1C and 1D may be formed by doping impurities having a larger diffusion coefficient than that for the low resistivity regions 3, by doping impurities at different dose, or by subjecting them to thermal hysteresis more often than the low resistivity regions 3. The deeper low resistivity regions 7 can be formed by the same process as that of forming deep source and drain regions of a MISFET of double-diffused drain (DDD) structure if such MISFET is formed in the same substrate. Regions formed by the same process have equal depths and lateral diffusion lengths within a process tolerance. In this specification, this equality is called "substantially the same".

As described above, by forming the deeper low resistivity region 7 in the region adjacent to the wiring 2, an overlap region 5 between an outwardly diffused or oozed diffusion region 4 and a low resistivity region formed adjacent thereto can be made large. The contact resistance is considered to be increased correspondingly.

A monitor circuit was manufactured and resistance values were measured in order to evaluate the effects of reducing a contact resistance of the connection structure shown in FIG. 1D.

FIG. 2 is a plan view showing the layout of the monitor circuit for evaluating the effects of reducing a contact resistance. Wirings 2 and low resistivity regions 3 and 3a are alternately and serially connected as shown in FIG. 2. A deeper low resistivity region 7 such as shown in FIG. 1D is being formed at the connection region between the wiring 2 and low resistivity region 3 and 3a. Side wall oxide are not shown in the figure.

The wiring 2 is of a two-layer structure made of polycrystalline silicon layer having a thickness of 0.1 μm and tungsten silicide layer having a thickness of 0.1 μm. A length L₁ from one center of the connection region of the wiring 2 to the adjacent center is 3.4 μm and a width W₁ of the wiring 2 is 0.75 μm. A length L₂ from one center of the connection region under the wiring 2 to the center of the adjacent wiring 2 is 3.3 μm and a width W₂ of the low resistivity regions 3 and 3a parallel to the wiring 2 is 1.0 μm.

Next, with reference to FIG. 1D, the conditions of forming each low resistivity region will be described. The oozed diffusion region 4 was formed by implanting phosphorus (P) ions into the wiring 2 at an acceleration energy of 40 keV and at a dose of 6×10¹⁵ cm⁻² and thereafter by performing heat treatment twice at 900° C. for 10 minutes.

The low resistivity region 7 was formed by implanting phosphorus (P) at an acceleration energy of 40 keV and at a dose of 3×10¹⁵ cm⁻², and the low resistivity region 3a was formed by implanting phosphorus (P) at an acceleration energy of 40 keV and at a dose of 4×10¹³ cm⁻². The low resistivity region 3a was formed by implanting arsenic (As) at an acceleration energy of 50 keV and at a dose of 4×10¹⁵ cm⁻². Each region was activated by performing heat treatment twice at 900° C. for 10 minutes. As indicated by broken lines 7a shown in FIG. 1D, the low resistivity region 7 was formed by implanting ions only in the regions having a width of 0.2 μm from both the ends of the wiring 2.

The side walls 6 were formed by depositing an oxide film having a thickness of 0.2 μm by chemical vapor deposition (CVD) and anisotropically etching it.

The monitor circuit shown in FIG. 2 having 50 connections regions, including 26 wirings 2 and 25 low resistive regions 7, was manufactured, and the resistance value across both the ends of the monitor circuit was measured. The resistance value of the monitor circuit was 15 kΩ. The resistance of one wiring 2 was about 70 Ω and the resistance of one low resistivity region was about 230 Ω. It is therefore understood that the resistance at one connection region between the wiring 2 and low resistivity region is about 150 Ω.

A similar monitor circuit having the connection structure of FIG. 1B was manufacture. The resistance at one connection region was about 250 Ω. It was found therefore that the resistance at the connection region could be lowered by about 40% by forming the deep low resistance region such as shown in FIG. 1C or 1D.

An embodiment which applies the fundamental structure shown in FIG. 1C to an SRAM cell will be described.

FIG. 3A is an equivalent circuit of an SRAM cell, and FIG. 3B is a plan view showing a layout of the circuit of FIG. 3A formed on a substrate.

As shown in FIG. 3A, a load resistor L1 is serially connected to the drain terminal D1 of a driver transistor Tr1 to constitute a serial circuit. A terminal of this serial circuit on the load resistor L1 side is connected to a power source voltage V_(DD), and the source terminal S1 of the driver transistor Tr1 is connected to ground potential GND. Similarly, a serial circuit of a load resistor L2 and a driver transistor Tr2 is formed and connected across the power source voltage V_(DD) and ground potential GND.

An interconnection point X1 between the drain terminal D1 of the driver transistor Tr1 and the load resistor L1 is connected to the gate electrode G2 of the other driver transistor Tr2. An interconnection point X2 between the drain terminal D2 of the driver transistor Tr2 and the load resistor L2 is connected to the gate electrode G1 of the other driver transistor Tr1.

The interconnection point X1 is also connected via a transfer transistor Tr3 to a bit line Bl1. Similarly, the interconnection point X2 is also connected via a transfer transistor Tr4 to a bit line BL2. Both the gate electrodes G3 and G4 of the transfer transistors Tr3 and Tr4 are connected to a word line WL. The terminals of the transfer transistors Tr3 and Tr4 connected to the interconnection points X1 and X2 are called source terminals S3 and S4, and the terminals thereof connected to the bit lines BL1 and BL2 are called drain terminals D3 and D4 in the specification.

As shown in FIG. 3B, active regions A1 and A2 are defined by a field oxide film formed on the surface of a silicon substrate. The driver transistors Tr1 and Tr2 and transfer transistor Tr4 are formed in the active region A1, and the transfer transistor Tr3 is formed in the active region A2. The gate, source, and drain of each transistor is represented by suing the same reference symbols (character and number) as those of a corresponding terminal shown in FIG. 3A.

The gate electrode G1 of the driver transistor Tr1 is connected at a connection region C1 to the source region S4 of the transfer transistor Tr4 and to the drain region D2 of the driver transistor Tr2. The connection region is a region where the surface of the silicon substrate is exposed by removing the gate oxide film formed on the surface of the active region.

The gate electrode G2 of the driver transistor Tr2 is connected at a connection region C2 to the source region S3 of the transfer transistor Tr3, and at a connection region C3 to the drain region D1 of the driver transistor Tr1. The source regions S1 and S2 of the driver transistors Tr1 and Tr2 are connected at a connection region C4 to a ground line GND.

Although not shown in FIG. 3B, the load resistors L1 and L2 are formed over an interlayer insulating film along the gate electrodes G1 and G2. One ends of the load resistors L1 and L2 are connected to the gate electrodes G1 and G2 near the connection regions C1 and C2. The other ends of the load resistors L1 and l2 are connected to a power source line formed in the same layer as the resistors L1 and L2 along the GND line.

Bit lines are formed in the lateral direction of FIG. 3B over an interlayer insulating film covering the load resistors L1 and L2 and power source line, along the gate electrodes G1 and G2. The bit lines are connected to the drain regions D3 and D4 of the transfer transistors Tr3 and Tr4 via contact holes.

The fundamental structure shown in FIG. 1C is utilized at the connection regions C1 to C4 of FIG. 3B.

Next, with reference to FIGS. 4A to 4E, a method of manufacturing an SRAM cell such as shown in FIG. 3B will be described. FIGS. 4A to 4E are cross sectional views taken along one-dot chain line IV--IV of FIG. 3B. A cross sectional view explaining the process of forming a MOSFET Tr5 of a DDD structure in another region of the same substrate is shown, by reference, at the right side of each cross sectional view.

FIG. 4A is a cross sectional view of a substrate after a process of forming openings of connection regions. A p-type well 10 is first formed on an n-type silicon substrate. Although only a p-type well is formed, other wells may also be formed. Isolating oxide regions 11 are formed to a film thickness of about 400 to 500 nm at predetermined areas by local oxidation.

An SiN film used as a mask for local oxidation is removed, and the surface of the exposed p-type well 10 is thermally oxidated to form a gate oxide film 12 to a thickness of about 20 nm. The gate oxide film 12 at the regions corresponding to connection regions C1 and C4 is removed by utilizing photolithography. In the above manner, the connection regions C1 and C4 are defined.

FIG. 4B is a cross sectional view of the substrate after a process of implanting ions for deep source and drain regions of a transistor having a DDD structure. A polycrystalline silicon layer is deposited to a thickness of about 300 nm over the whole surface of the substrate by CVD. Next, phosphorus ions are implanted in the polycrystalline silicon layer at an acceleration energy of 30 to 70 keV and at a dose of 1×10¹⁵ to 10×10¹⁵ cm⁻².

The polycrystalline silicon layer is patterned to form the gate electrode G1 of the driver transistor Tr1, the gate electrode G4 of the transfer transistor Tr4, and the ground line GND at the connection region C4. At this time, the gate electrode G5 of MOSFET having a DDD structure is formed.

Instead of the polycrystalline silicon layer, a two-layer structure of a polycrystalline silicon layer and a tungsten silicide layer may be used. For example, a polycrystalline silicon layer is deposited to a thickness of 100 nm, and a tungsten silicide layer is deposited thereon to a thickness of 100 nm.

Other layers may also be used for the conductive layer G, which include a single layer structure of an amorphous silicon layer, a two-layer structure of a polycrystalline silicon layer and a silicide layer, a three-layer structure of an amorphous silicon layer, a polycrystalline silicon layer, and a silicide layer, a three-layer structure of a polycrystalline silicon layer, a silicide layer, and an amorphous silicon layer, and a four-layer structure of an amorphous silicon layer, a polycrystalline silicon layer, a silicide layer, and another amorphous silicon layer.

The region of MOSFET with the DDD structure and the connection regions C1 and C4 are exposed, and other regions are covered with a resist pattern 13. Next, by using the resist pattern 13 as a mask, impurity ions are implanted for forming the source and drain regions of MOSFET Tr5 with the DDD structure. In this ion implantation, impurity ions having a larger diffusion coefficient among the two kinds of impurities for the source and drain regions are used. For example, phosphorus ions are implanted at an acceleration energy of 30 to 70 keV and a dose of 1×10¹⁵ to 5×10¹⁵ cm⁻². With this impurity ion implantation, the deep source and drain regions S5a and D5a of MOSFET Tr5 with the DDD structure are formed. At this time, the low resistance regions 14 and 15 are formed at the connection regions C1 and C4.

FIG. 4C is a cross sectional view of the substrate after a process of forming shallow source and drain regions of MOSFET with the DDD structure and the source and drain regions of each transistor of the SRAM cell and forming an interlayer insulating film. The resist pattern shown in FIG. 4B is removed. By using the gate electrode of each transistor and the isolating oxide regions as a mask, impurity ions are implanted for forming the shallow source and drain regions of MOSFET with the DDD structure. In this ion implantation, impurity ions having a smaller diffusion coefficient among the two kinds of impurities for the source and drain regions are used. For example, arsenic ions are implanted at an acceleration energy of 30 to 70 keV and a dose of 1×10¹⁵ to 10×10¹⁵ cm⁻².

With this impurity ion implantation, the shallow source and drain regions S5b and D5b of MOSFET Tr4 with the DDD structure are formed. At this time, the source and drain regions S4 and D4 of the transfer transistor Tr4 and the shallow low resistivity region 15a over the low resistivity region 15 at the connection region C4 are formed. Part of the source region S4 is formed over the low resistivity region 14.

The source and drain regions are formed by the above processes through ion implantation. At this stage, impurities are not still activated, but they are activated by later annealing.

Next, an interlayer insulating film 16 of SiO₂ is deposited by CVD on the whole surface of the substrate to a thickness of about 100 nm. A contact via hole is formed by utilizing photolithography to expose the surface of the gate electrode G1 at a predetermined area.

FIG. 4D is a cross sectional view of the substrate after a process of forming load resistors and a power source line. A polycrystalline silicon layer 19 is formed by CVD over the whole surface of the substrate to a thickness of 100 nm. Impurities are doped into the polycrystalline silicon layer 19 at the region where the resistance is to be lowered. In this embodiment, by using a resist pattern as a mask, arsenic ions are implanted into the region along the ground line GND, for example, at an acceleration energy of 30 to 70 keV and a dose of 1×10¹⁵ to 10×10¹⁵ cm⁻². The lowered resistance region is used as the power source line.

After arsenic ions are implanted, annealing is performed at 900° C. for 10 minutes. This annealing activates the impurity ions implanted by the previous processes. At the region of MOSFET Tr5 with the DDD structure, phosphorus ions having a relatively large diffusion coefficient implanted at the process explained with FIG. 4B are deeply diffused and at the same time activated to thereby form the deep source and drain regions S5a and D5a. In addition, arsenic ions having a relatively small diffusion coefficient implanted at the process explained with FIG. 4C are slightly diffused and at the same time activated to thereby form the shallow source and drain regions S5b and D5b. The source and drain regions S4 and D4 of the transistor Tr4 are also activated.

With this annealing, phosphorus ions in the gate electrode G1 are diffused into the polycrystalline silicon layer 19 near at the connection region C1. Therefore, the gate electrode G1 and polycrystalline silicon layer 19 are electrically connected together by a low resistance region at the connection boarder therebetween.

Also at the connection regions C1 and C4, phosphorus ions implanted at the process explained with FIG. 4B are deeply diffused and activated so that the low resistivity regions 14 and 15 are formed. The low resistivity region 14 partially overlaps the source region S4 and is electrically connected thereto. At the connection region C4, impurities in the low resistivity region 15 are activated. The shallow low resistivity region 15a is connected, as shown in FIG. 3B, to the source region S1 of the driver transistor Tr1. Therefore, the low resistivity region 15 is electrically connected via the shallow low resistivity region 15a to the source region S1.

At the same time, at the connection regions C1 and C4, phosphorus ions in the gate electrode G1 and ground line GND in contact with the p-type well 10 are diffused into the p-type well 10 to thereby form the oozed diffusion regions 17 and 18.

Next, the polycrystalline silicon layer 19 is patterned to form the power source line and load resistors L1 and L2 (FIG. 3A). The power source line is formed along the ground line GND when viewed in the layout of FIG. 3B. One ends of the load resistors L1 and L2 are connected to the gate electrodes G1 and G2 near the connection regions C1 and C2 when viewed in the layout of FIG. 3B, and the other ends are connected to the power source line formed along the ground line GND.

FIG. 4E is a cross sectional view of the substrate after a process of forming bit lines. After the power source line and load resistors are formed by patterning the polycrystalline silicon layer 19, an interlayer insulating film 20 is formed by depositing by CVD an SiO₂ film to a thickness of about 100 nm and a phosphorus silicate glass (PSG) film to a thickness of about 500 nm. Reflow is performed thereafter at 900° C. for about 10 minutes to planarize the surface of the interlayer insulating film 20. With this heating, the low resistivity regions 14 and 15 and other regions activated by annealing at the process explained with FIG. 4D are further deeply diffused. Therefore, the contact resistance at the connection regions between the ground line GND and low resistivity region 15 and between the gate electrode G1 and low resistivity region 14 is further lowered.

Next, a contact hole is formed to partially expose the surface of the drain region D4 of the transfer transistor Tr4. An aluminum layer 21 is deposited to a thickness of about 1 μm by physical vapor deposition (PVD), and patterned to form the bit lines.

With the above processes, the SRAM cell shown in FIG. 3A can be formed.

At the same time when the deep source and drain regions S5a and D5a of the transistor Tr5 with the DDD structure are formed, the low resistivity regions 14 and 15 are formed at the connection regions. Therefore, the overlap regions between the low resistivity regions 14 and 15 and the oozed diffusion regions 17 and 18 just under the wiring and the gate electrode are made large. At the connection region C4 formed by the above processes, the length of the deep low resistivity region 15 creeping under and overlapping the GND line is considered to be about 0.3 to 0.4 μm, and the length of the shallow low resistivity region 15a creeping under the GND line is considered to be about 0.1 μm.

Since the overlap regions between the low resistivity regions 14 and 15 and the oozed diffusion regions 17 and 18 can be made larger, the contact resistance between the wiring formed at the same time when the gate electrodes are formed and the low resistivity region formed adjacent to the wiring can be lowered.

In a usual SRAM, transistors with the DDD structure are used for circuits which require a large source/drain breakdown voltage, such as an input protection circuit for preventing electrostatic breakdown and a redundancy circuit with fuses. Such circuits can be manufactures by the SRAM cell manufacturing method explained with FIGS. 4A to 4E without increasing manufacturing steps.

In the above embodiment, after ions are implanted for forming the deep source and drain regions of the DDD structure at the process explained with FIG. 4B, the resist pattern 13 is removed, and immediately thereafter ion implantation is performed for the shallow source and drain regions. Annealing may be performed between the processes of forming the deep and shallow source and drain regions. The deep low resistivity regions 14 and 15 are shown in FIG. 4D can be diffused deeper by this annealing. Therefore, the overlap regions between the oozed diffusion regions 17 and 18 and the low resistivity regions 14 and 15 can be made larger and the contact resistance can be further lowered.

If annealing is performed between the processes of implanting impurity ions for the double source and drain regions of the DDD structure, the same species of impurity ions may be used.

The DDD structure may also be formed by vapor phase diffusion or by deposition of diffusion species and drive-in, instead of ion implantation. Also in this case, either two kinds of impurities having different diffusion coefficients may be diffused at the same time, or the same kind of impurities may be diffused twice.

In the method described with FIGS. 4A to 4E, a MOSFET with a single drain structure is used as the transistor of an SRAM cell. A lightly doped drain (LDD) structure may be used. In forming an LDD structure, after the process illustrated in FIG. 4B, the resist pattern 13 is removed and LDD regions are formed before ion implantation is performed for the shallow source and drain regions S5b and D5b.

By using the gate electrode of each transistor as a mask, phosphorus ions are implanted at an acceleration energy of 40 keV and at a dose of 4×10¹³ cm⁻². Next, an SiO₂ film is deposited to a thickness of about 200 nm by CVD, and anisotropically etched by reactive ion etching or other methods to form side wall oxide regions on the side walls of the gate electrodes. Thereafter, the processes same as the process illustrated in FIG. 4C and the following process are performed.

The LDD structure can prevent a device performance from being deteriorated by the hot electron effect accompanied by fine pattern devices.

In the methods explained with FIGS. 4A to 4E, impurities implanted in the deep source and drain regions of the DDD structure are also implanted to all the connection regions. Impurities may be implanted only into limited connection regions. For example, impurities may be implanted only into the connection region C4 at which the ground line GND is connected.

For example, the low resistivity region 14 shown in FIG. 4E is formed also at the partial area of the source region S4. It is conceivable that the shape of the source region may change and the transistor characteristics may be adversely affected.

The connection regions C1, C2, and C3 shown in FIG. 3B overlap the isolating oxide regions. Therefor, impurity ions for forming the low resistance region are also implanted into the area near the boarder between the active region A1 and the isolating oxide region. Impurities implanted into the area near the boarder creep under the isolating oxide region at the later annealing. Therefore, the isolation function may be damaged. To solve these possible problems, deep ion implantation can be arranged not to be performed at the connection regions C1, C2, and C3.

As above, although the embodiment of the invention lowers the contact resistance between a wiring and a low resistivity region, the adverse effect may occur depending on a connection region where ions are implanted. Whether or not the embodiment of the invention is applied, is preferably determined from a trade-off between the lowered resistance and the adverse effect at each connection region.

The present invention has been described in connection with the preferred embodiments. The invention is not limited only to the above embodiments. It is apparent to those skilled in the art that various modification, improvements, combinations and the like can be made without departing from the scope of the appended claims. 

I claim:
 1. A semiconductor device comprising:a semiconductor substrate having a surface region of a first conductivity type; a conductive film directly formed on part of a surface of said surface region, said conductive film containing impurities of a second conductivity type opposite to the first conductivity type; an oozed diffusion region of the second conductivity type formed by diffusion of the impurities in said conductive film, said oozed diffusion region being formed in said surface region at a first area containing said part and being contiguous to said conductive film; a low resistivity region of the second conductivity type formed in said surface region, extending from a second area outside of the conductive film to a third area under said conductive film, and merged with said oozed diffusion region; and a double-diffused drain (DDD) structure transistor comprising a first gate electrode formed on a gate insulating film over a channel region defined by a fourth area in said surface region, first source and drain regions of the second conductivity type formed on both sides of said first gate electrode, and second source and drain regions of the second conductivity type formed on both sides of said first gate electrode, said second source and drain regions having a larger depth from said surface than said first source and drain regions, enclosing said first source and drain regions in said surface region, and extending to fifth areas under said first gate electrode, wherein said conductive film has substantially the same layer structure as said first gate electrode, said low resistivity region has substantially the same depthwise impurity concentration profile as said second source and drain regions, and a length of a portion of said low resistivity region under said conductive film is substantially the same as a length of a portion of said second source and drain regions under said first gate electrode.
 2. A semiconductor device according to claim 1, further comprising a first shallow low resistivity region of the second conductivity type formed shallower than said low resistivity region, said first shallow low resistivity region being enclosed in said low resistivity region in a region near said conductive film and extending under said conductive film slightly from an end thereof, wherein a length of a portion of said first shallow low resistivity region under said conductive film slightly from an end thereof is substantially the same as a length of a portion of said first source and drain regions under said first gate electrode.
 3. A semiconductor device according to claim 2, wherein impurities of said low resistivity region have a larger diffusion coefficient than impurities of said first shallow low resistivity region.
 4. A semiconductor device according to claim 2, wherein said conductive film has a structure selected from the group consisting of a single layer structure of a polycrystalline silicon layer, a single layer structure of an amorphous silicon layer, a two-layer structure of a polycrystalline silicon layer and a silicide layer, a two-layer structure of an amorphous silicon layer and a silicide layer, a three-layer structure of an amorphous silicon layer, a polycrystalline silicon layer, and a silicide layer, a three-layer structure of a polycrystalline silicon layer, a silicide layer, and an amorphous silicon layer, and a four-layer structure of an amorphous silicon layer, a polycrystalline silicon layer, a silicide layer, and another amorphous silicon layer, each stacked in the recited order.
 5. A semiconductor device according to claim 1, further comprising:a second shallow low resistivity region of the second conductivity type formed shallower than said low resistivity region, said second shallow low resistivity region being enclosed in said low resistivity region in a region near said conductive film and extending under said conductive film slightly from an end thereof; an LDD structure transistor comprising a second gate formed on a gate insulating film over a channel region defined by a sixth area in said surface region, low impurity concentration source and drain regions extending to seventh areas under said second gate electrode slightly from an end thereof, side wall insulating regions formed on both sides of said second gate electrode, and high impurity concentration source and drain regions having a higher impurity concentration source and drain regions having a higher impurity concentration than, and being electrically connected to, said low impurity concentration source and drain regions, said high impurity concentration source and drain regions extending to eighth areas under said side wall insulating regions slightly from an end thereof, wherein a length of a portion of said second shallow low resistivity region under said conductive film slightly from the end thereof is substantially the same as a length of a portion of said low impurity concentration source and drain regions under said second gate electrode slightly from the end thereof.
 6. A semiconductor device according to claim 5, wherein said conductive film has a structure selected from the group consisting of a single layer structure of a polycrystalline silicon layer, a single layer structure of an amorphous silicon layer, a two-layer, structure of an amorphous silicon layer and a silicide layer, a three-layer structure of an amorphous silicon layer, a polycrystalline silicon layer, and a silicide layer, a three-layer structure of a polycrystalline silicon layer, a silicide layer, and an amorphous silicon layer, and a four-layer structure of an amorphous silicon layer, a polycrystalline silicon layer, a silicide layer, and another amorphous silicon layer, each stacked in the recited order.
 7. A semiconductor device according to claim 5, wherein the semiconductor device includes an SRAM cell having said LDD structure transistor and said conductive film constitutes a local interconnect of said SRAM cell.
 8. A semiconductor device according to claim 1, wherein said conductive film has a structure selected from the group consisting of a single layer structure of a polycrystalline silicon layer, a single layer structure of an amorphous silicon layer, a two-layer structure of a polycrystalline silicon layer and a silicide layer, a two-layer structure of an amorphous silicon layer and a silicide layer, a three-layer structure of an amorphous silicon layer, a polycrystalline silicon layer, and a silicide layer, a three-layer structure of a polycrystalline silicon layer, a silicide layer, and an amorphous silicon layer, and a four-layer structure of an amorphous silicon layer, a polycrystalline silicon layer, a silicide layer, and another amorphous silicon layer, each stacked in the recited order.
 9. A semiconductor device according to claim 1, wherein the semiconductor device includes an SRAM cell and said conductive film constitutes a local interconnect of the SRAM cell.
 10. A semiconductor device according to claim 9, wherein said DDD structure transistor constitutes a peripheral circuit for said SRAM cell.
 11. An SRAM semiconductor device formed on a semiconductor substrate, including a parallel circuit of two serial circuits each having a MISFET driver transistor and a load, a pair of wirings each connecting an interconnection point between the driver transistor and the load of one of said serial circuits to a gate electrode of the driver transistor of the other of said serial circuits, and a MISFET transfer transistor connected to each of the interconnection points, wherein each of the driver transistors and the transfer transistors comprises a channel region defined in an active region of a first conductivity type in said semiconductor substrate, a gate insulating film formed on said active region, an insulated gate electrode formed on said gate insulating film over the channel region, and source/drain regions of a second conductivity type opposite to said first conductivity type formed in said active region on both sides of the insulated gate electrode and having a first depth from a surface of said semiconductor substrate,the SRAM semiconductor device comprising: an insulating layer including a field insulating layer for defining said active regions, and said gate insulating films, and having a contact hole in a vicinity of one of said source/drain regions of one of said driver transistors; one of said pair of wirings containing impurities of the second conductivity and formed partly on said insulating layer and partly directly on said active region exposed in said contact hole; a diffusion region of said second conductivity type formed in said active region under a portion of said one wiring disposed in said contact hole, by diffusion from said one wiring; a double-diffused drain (DDD) structure MISFET having another channel region defined in an active region of the first conductivity type in the surface of said semiconductor substrate, another source/drain regions of the second conductivity type and of a DDD structure formed on both sides of said another channel region and comprising shallow source/drain regions and deep source/drain regions enveloping said shallow source/drain regions and having a second depth larger than said first depth, and another insulated gate electrode formed over said another channel region; a first connection region of said second conductivity type formed in said active region adjacent to said one wiring, having a third depth which is substantially the same as said second depth, merging with said one source/drain region of said one driver transistor and with said diffusion region, and extending under said portion of said one wiring from an end thereof, wherein a length of said first connection region under said one wiring is substantially the same as a length of said deep source/drain region under said another insulated gate electrode of the DDD structure.
 12. An SRAM semiconductor device according to claim 11, wherein said insulating layer has another contact hole in a vicinity of one of said source/drain regions of one of said transfer transistors, the other of said pair of wirings is continuous to said gate electrode of said one driver transistor and extends to a portion of an active region exposed in said another contact hole, further comprising:another diffusion region of said second conductivity type formed in said active region under a portion of said other wiring disposed in said another contact hole, by diffusion from said other wiring; a second connection region of said second conductivity type formed in said active region adjacent to said other wiring, having a fourth depth which is substantially the same as said second depth, merging with said one source/drain region of said one transfer transistor and with said another diffusion region, and extending under said other wiring from an end thereof, wherein a length of said second connection region under said other wiring is substantially the same as a length of said deep source/drain region under said another insulated gate electrode of the DDD structure.
 13. An SRAM semiconductor device according to claim 12, wherein said insulating layer has a further contact hole in a vicinity of one of said source/drain regions of the other of said driver transistors, said other of said pair of wirings is continuous to said gate electrode of said one driver transistor and extends to a portion of an active region exposed in said further contact hole, further comprising:further diffusion region of said second conductivity type formed in said active region under a portion of said other wiring disposed in said further contact hole, by diffusion from said other wiring; a third connection region of said second conductivity type formed in said active region adjacent to said other wiring, having a fourth depth which is substantially the same as said second depth, merging with said one source/drain region of said other driver transistor and with said further diffusion region, and extending under said other wiring from an end thereof, wherein a length of said third connection region under said other wiring is substantially the same as a length of said deep source/drain region under said another insulated gate electrode of the DDD structure.
 14. An SRAM semiconductor device according to claim 12, wherein said source/drain regions of said driver transistors and said transfer transistors have an LDD structure.
 15. An SRAM semiconductor device according to claim 11, wherein said insulating layer has a further contact hole in a vicinity of one of said source/drain regions of the other of said driver transistors, the other of said pair of wirings is continuous to said gate electrode of said one driver transistor and extends to a portion of an active region exposed in said further contact hole, further comprising:further diffusion region of said second conductivity type formed in said active region under a portion of said the other wiring disposed in said further contact hole, by diffusion from said the other wiring; a third connection region of said second conductivity type formed in said active region adjacent to said the other wiring, having a fourth depth which is substantially the same as said second depth, merging with said one source/drain region of said other driver transistor and with said further diffusion region, and extending under said other wiring from an end thereof, wherein a length of said third connection region under said other wiring is substantially the same as a length of said deep source/drain region under said another insulated gate electrode of the DDD structure.
 16. An SRAM semiconductor device according to claim 11, wherein said source/drain regions of said driver transistors and said transfer transistors have an LDD structure. 